阻燃玛蹄脂使用范围

Flame-retardant Ma foot fat
It is made of chemical bonding agent, film forming agent, thickening agent and mineral filler and adding a proper amount of flame retardant. It has the characteristics of air tightness, waterproof, 

阻燃玛蹄脂技术参数 　　

1;外 观 ：          黑色糊状
2；挥发物：                5±25%
3；氧指数：            ＞30%（OI）
4;粘结力：             20℃1.5kg/cm2
5；比重：                  1600～1700kg/m3
6;阻燃性：                 B2级。（离开火源1秒钟自熄。）
7;耐热性：                在95℃温度下，45度斜搁4小时，温度升到120℃，45度斜搁1小时无流淌起泡现象。
8抗冻性：                 -170℃～+120℃各悬挂2小时无开裂、无脱离。
9；使用温度：  -170~120℃
10;吸 水 率：   室温浸泡24小时，吸水量不大于试料重量的1%。
11;施工厚度：  6mm
12;干燥时间：  手指接触1小时，全干60小时。
13;施 工 量  每平方米12kg（含损耗）
14;包装规格　：　       35Kg/铁桶

anti-freezing, not easy to crack and aging, cold construction at room temperature, flame retardant and waterproof after drying. It is used as a moisture-proof layer on the surface of heat preservation and cooling layer, and as an outer protective material matching with cement, foam glass,

阻燃玛蹄脂使用方法：
1、将玛蹄脂涂在泡沫玻璃或非深冷部位。等隔热材料外表，涂层3mm，并在中间隔一层防水玻璃布或塑料窗纱。在**遍玛蹄脂稍干后，方可涂抹*二遍玛蹄脂，干固后，总厚度达到6mm。
2、涂布均匀，光滑平整，表面无起泡。
Technical parameters of flame-retardant Ma foot fat
贮存与运输：贮存温度为-5℃—45℃,避免暴晒。自出厂之日起，贮存期为2年；运输时不得倾斜或横放，应注意使容器不要损害。 　 hard microcellular calcium silicate and polyurethane foam. It is widely used in petroleum, chemical, textile, pharmaceutical and other industries.　
　　
注意事项： 　　1、 搬运过程中轻搬、轻放，防止包装破裂。 　　2、 存放于阴凉处，避免阳光爆晒。 　　3、 施工现场要通风，有利于干燥。 　　
               4、 施工后剩余玛蹄脂要密封保存。

The effect of flame retardant Ma hoof fat: 1, the end seal, 2, heat preservation and waterproof anticorrosion will apply the martre ester evenly to the exterior of thermal insulation material, not only can achieve the best sealing property, but also the Ma hoof grease is also a kind of heat preservation and locking material, which can lock the heat of the process in the pipe preparation, and can reduce the application of the heat insulation engineering. Working thickness, material cost saving, Ma foot grease itself added high performance corrosion inhibitor, can effectively prevent the external entry of chemical and physical effects, prevent moisture and moisture permeability of insulation insulation material, avoid the reduction of insulation efficiency.